AIE ABS S20G2
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5GD97g_AIE-ABS-S20G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AIE ABS S20G2 is an Acrylonitrile Butadiene Styrene (ABS) material filled with 10% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of AIE ABS S20G2: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 4 | 4900 | MPa | ASTM D790 |
| Flexural Strength 5 | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 0.125 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 200 to 240 | °C | |
| Middle Temperature | 200 to 240 | °C | |
| Front Temperature | 200 to 240 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExxonMobil™ PP1064L1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| GUR® 4120 | Celanese Corporation | UHMWPE | GUR® |
| Hostacom BB 1161 F M 2678 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Pibiflex® 4612 NATURALE | SO.F.TER. SPA | TPC-ET | Pibiflex® |
| Braskem PE SGM9450F | Braskem | HDPE | Braskem PE |