LNP™ THERMOTUF™ PF006I compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5FxzuV_LNP-THERMOTUF-PF006I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* PF006I is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound PF-1006 HI Product reorder name: PF006I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 to 2.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.62 to 0.67 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.83 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.83 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16200 | MPa | ASTM D638 |
| -- | 9650 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2/5 |
| Break 3 | 97.4 | MPa | ASTM D638 |
| Break | 99.0 | MPa | ISO 527-2/5 |
| Tensile Elongation 4(Break) | 8.2 | % | ASTM D638 |
| Flexural Modulus 5(50.0 mm Span) | 6830 | MPa | ASTM D790 |
| Flexural Strength 6(Break, 50.0 mm Span) | 158 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 730 | J/m | ASTM D4812 |
| 23°C 8 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.0 | J | ASTM D3763 |
| -- | 4.98 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 135 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ PRM-55C | Muehlstein | PP Random Copolymer | CERTENE™ |
| Fainplast PVC HGKA 79/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| FHR Polypropylene 43S2A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Durolon® VR2000 CR010 | Unigel Plásticos | PC | Durolon® |
| TechnoElast S A9000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |