RTP 100 HI UV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5F4WKv_RTP-100-HI-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1030 | MPa | ASTM D638 |
| Tensile Strength | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 23.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1500 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 102 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D-955, 0.25in.: 25mil/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 213 - 268 | °C | |
| Middle Temperature | 213 - 268 | °C | |
| Front Temperature | 213 - 268 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F662E13 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| POLYMAN® (ABS) LP 137 A | A. Schulman Europe | ABS | POLYMAN® |
| Purell RP315M | LyondellBasell Industries | PP Random Copolymer | Purell |
| LUBEMID B27 GF30 FR V0 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| LNP™ THERMOCOMP™ RF006L compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |