CELEX™ 310HF.M
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5EbGgZ_CELEX-310HF-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CELEX™ 310HF.M glass fiber reinforced polycarbonate resin is a 10% glass fiber reinforced polycarbonate material. It provides a property balance of easy flow, superior ignition resistance, high rigidity, dimension stability and heat resistance. It provides the injection molded part with good aesthetics. It does not contain Chlorine/or Bromine and phosphate type flame retardants. It is designed for a wide range of applications, e.g. computer enclosures, electronic accessories and electrical appliances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 4000 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 118 | °C | |
| 1.8 MPa, Unannealed | 112 | °C | |
| Vicat Softening Temperature | 132 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.00 mm, WT and RD | V-1 | ||
| 1.00 mm, BK and NC | V-0 | ||
| 1.60 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 271 to 310 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6300HH | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Xuchuan XCW-120N | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| EMAC+® SP1330 | Westlake Chemical Corporation | EMA | EMAC+® |
| Sylvin 7833-70C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 140 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |