RELENE® LL36RA045
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5DiKib_RELENE-LL36RA045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LL36RA045 is a Butene Comonomer based Linear Medium Density Polyethylene. This grade when blended with appropriate carbon black can withstand continuous exposure. LL36RA045 when pulverised into 20-30 mesh powder offers good processability. This grade has very good Environmental Stress Crack Resistance (ESCR) and a combination of hardness and impact strength. This grade contains normal dose of antioxidant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | > 350 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 2.00 mm, Compression Molded) | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Compression Molded) | 588 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm, Injection Molded) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 A | RTP Company | Nylon 6 | RTP |
| TRANSMARE® 10HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| ECO PELLET® LC52A | UMG ABS, Ltd. | PLA+PC | ECO PELLET® |
| Fortron® 4332L6 | Celanese Corporation | PPS | Fortron® |
| MAJORIS AFR090 - 8229 | AD majoris | PP Copolymer | MAJORIS |