WPP PP PPC5GF2-Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5CpOie_WPP-PP-PPC5GF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC5GF2-Black is a polypropylene copolymer (PP Copoly) product, which contains a 20% glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 67.0 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/5 |
| Yield | 71.0 | MPa | ISO 527-2/50 |
| Fracture | 62.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 3600 | MPa | ASTM D790 |
| -- 3 | 3800 | MPa | ISO 178 |
| Flexural Stress 4 | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 92 | J/m | ASTM D256 |
| -40°C | 6.5 | kJ/m² | ISO 180 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 158 | °C | ISO 75-2/B |
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 147 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 146 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/Af |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1345 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| RTP 103 CC SI 2 | RTP Company | PP, Unspecified | RTP |
| Hyundai EP PA6 LS165 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LNP™ STAT-KON™ AE003 compound | SABIC Innovative Plastics Europe | ABS | LNP™ STAT-KON™ |
| Sylvin 8749-80AM Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |