HANWHA LLDPE 4300N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5CBfgw_HANWHA-LLDPE-4300N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 4300N is manufactured by Unipol process and designed for general purpose and agricultural film . LLDPE 4300N has well balanced property of mechanical property, processability and optical property |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 21.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | Internal Method |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 41.2 | MPa | |
| TD : Break, 30 µm | 37.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 650 | % | |
| TD : Break, 30 µm | 750 | % | |
| Dart Drop Impact (30 µm) | 140 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 117.7 | kN/m | |
| TD : 30.0 µm | 122.6 | kN/m |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow-up Ratio | 2.00 to 3.00 | ||
| Optimum Gage Range | 30.0 to 100.0 | µm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| Peak Melting Temperature | 122 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durepol® PBT A3 G30 CNZ0340 BT320 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Escorene™ Ultra AD 2528 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Polimid B 30 GF V0HFR KW | Poliblend S.p.a. | Nylon 6 | Polimid B |
| Sylvin 8280-70FUV White 1556 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8980-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |