ALCOM® PC 730/3.1 UV WT1283-09LDM
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5C3LGL_ALCOM-PC-730-3-1-UV-WT1283-09LDM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PC 730/3.1 UV WT1283-09LDM is a Polycarbonate (PC) product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Typical application: Lighting Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | 68.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | % | ISO 527-2 |
| Flexural Modulus | 2580 | MPa | ISO 178 |
| Flexural Stress | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 4.0 | kJ/m² | |
| -40°C | 4.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | 85 | kJ/m² | |
| -20°C | 120 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 0.750 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 960 850 | °C | |
| 4.00 mm | 960 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 1 | ISO 13468 | ||
| Total, 3000 µm | 58.0 | % | |
| Total, 4000 µm | 51.0 | % | |
| Haze | ISO 13468 | ||
| 1000 µm 2 | 93 | % | |
| 3000 µm 3 | 95 | % | |
| 4000 µm 4 | 95 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Half Power Angle - T(Y) 5 | |||
| 3.00 mm | 27.0 | ° | |
| 4.00 mm | 38.0 | ° |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 12 | hr | |
| Suggested Max Moisture | 0.010 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | A, 2° |
| 2 . | Ill. A, 2° |
| 3 . | A, 2° |
| 4 . | Ill. A, 2° |
| 5 . | A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-756 | CHI MEI CORPORATION | ABS | POLYLAC® |
| Rhelon G1533H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Huafon JF-W-AH6065 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| KEBATER® PBT BF115 | BARLOG plastics GmbH | PBT | KEBATER® |
| Hifax TRC 277P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |