AKROMID® B3 ICF 40 black (5020)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5C29nG_AKROMID-B3-ICF-40-black-5020-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.10 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.9 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 1.8 | 2.5 | % | ISO 178 |
| Tensile Modulus | 32000 | 13600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 220 | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 25000 | 17000 | MPa | ISO 178 |
| Flexural Stress 3 | 320 | 215 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 60 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.7E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.3E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+3 | -- | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 299/2 GL | A. Schulman Europe | ABS | POLYMAN® |
| Quadrant EPP Corzan® CPVC | Quadrant Engineering Plastic Products | CPVC | Quadrant EPP |
| Andur 85 APLF/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Geon™ 210 Series 215 Blending Resin | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 210 Series |
| EMPILON® 639A | EMPILON | SEBS | EMPILON® |