LubriOne™ AT-000/10T
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5BCz29_LubriOne-AT-000-10T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 46.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 to 6.0 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.39 | ||
| vs. Steel - Static | 0.23 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 48 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 154 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 188 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO AES W270 | Techno Polymer Co, Ltd. | AES | TECHNO AES |
| Ultramid® C40LX 01 | BASF Corporation | Nylon 66/6 | Ultramid® |
| Nucrel® 0407HS | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| ALTECH® PA66 A 2030/109 GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Karina NATURAL PVC COMPOUND 800-25/ 1-AYR-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |