Borstar® HE6063

Category:	HDPE , High Density Polyethylene
Manufacturer:	Borealis AG
Trademark:	Borstar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5Aa4uc_Borstar-HE6063.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Borstar HE6063 is a natural, UV-stabilised, colourable, bimodal high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology.

Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).

Borstar HE6063 contains a well dispersed UV-stabiliser in sufficient amount providing a measure of weathering resistance. In order to fully utilise the unique low shink properties of Borstar HE6063 we recommend the use of non-warping colour masterbatches.

The physical toughness and very low water permeability of the compound make it an ideal solution especially for buried power cables. Borstar HE6063 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.

Borstar HE6063 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure:

ASTM D 1248 Type III, Class A, Category 4, Grade E9, J5

BS 6234: Type H03, TS2

DIN 57818/VDE 0818

EN 50290-2-24

D 620 S1, Part 1, table 4B, DMP 5, 13, 16

IEC 60502, Type ST7

IEC 60840, Type ST7

ISO 1872-PE, KHLN, 45 D-006

NF C32-060

General Information
Additive	UV stabilizer
Features	Moisture resistance High ESCR (Stress Cracking Resistance) Good UV resistance Workability, good Good coloring Good wear resistance Scratch resistance Good weather resistance Good toughness Low shrinkage High hardness
Uses	Communication Cable Jacketing Cable sheath Wire and cable applications
Agency Ratings	ASTM D 1248, II, Class A, Cat. 4, Grade E9 , J5 BS 6234 Type H03 TS2 EN 50290-2-24 HD 620 S1 Part 1, table 4B, DMP 5, 13, 16 ICEA S-61-402 IEC 60502 Type ST7 IEC 60840 Type ST7 NF C 32-060
Appearance	Natural color
Forms	Particles
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density ¹(Base Resin)	0.946	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	0.50	g/10 min	ISO 1133
190°C/5.0 kg	2.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (Condition B, 50°C, 10% Igepal, F0)	> 5000	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness
Shaw D, 1 sec	61		ISO 868
Shaw D, 3 seconds	60		DIN 53505

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	35.0	MPa	ISO 527-2/50
Tensile Strain (Break)	900	%	ISO 527-2/50
Flexural Modulus	850	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	10	ohms·cm	IEC 60093
Dielectric Strength	70	kV/mm	IEC 60243-1

Additional Information	Nominal Value	Unit	Test Method
Pressure Test ²(115°C)		%	IEC 60811-3-1

Extrusion	Nominal Value	Unit
Melt Temperature	180 - 190	°C

Extrusion instructions
Preheating: 90 °CCooling water: 60 °C

Note Message
1 .	ISO 1872-2
2 .	at high temperature, 6 hrs

Resin Grade	Manufacturer	Category	Trademark
Sindustris ABS LLG824	Sincerity Australia Pty Ltd.	ABS	Sindustris ABS
TEKNIFLEX® VM100	Tekni-Films, a div of Tekni-Plex	Film, PVC	TEKNIFLEX®
TRIEL® 5301SP	Samyang Corporation	TPEE	TRIEL®
Natur-Tec® BF3002	Natur-Tec - Northern Technologies International Corp	Biodeg Polymers	Natur-Tec®
BESTNYL SI30VI02BWX	Triesa Plastics	Nylon 6	BESTNYL