MEGOLON™ S650

Category:	TP, Unspecified , Thermoplastic
Manufacturer:	AlphaGary
Trademark:	MEGOLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5A0zQo_MEGOLON-S650.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MEGOLON™ S650 is a thermoplastic, halogen free, fire retardant sheathing compound possessing both improved processing characteristics, and good all-round properties.

APPLICATIONS

CENELEC: HD 624.7 S1

UK: BS 7878:7

Germany: DIN VDE 0207 part 24 type HM4

General Information
Features	Flame Retardant Halogen Free
Uses	Cable Jacketing
Agency Ratings	BS 7878:7 DIN VDE 0207 Part 24, Type HM4
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.52	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (150°C/21.6 kg)	6.5	g/10 min	ISO 1133
Mooney Viscosity (ML 1+4, 140°C)	40	MU	ASTM D1646

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	54		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
-- ¹	14.0	MPa	IEC 60811-1-2
--	11.0	MPa	IEC 60811-1-1
Tensile Strain
Break ²	160	%	IEC 60811-1-2
Break	170	%	IEC 60811-1-1
Elongation at Break
after 4 hours, in IRM 902 Oil : 70°C	160	%
after 7 days, in IRM 902 Oil : 23°C	170	%
after 7 days, in IRM 903 Oil : 23°C	160	%
Tensile Strength
after 4 hours, in IRM 902 Oil : 70°C	9.50	MPa
after 7 days, in IRM 902 Oil : 23°C	11.0	MPa
after 7 days, in IRM 903 Oil : 23°C	9.00	MPa

Thermal	Nominal Value	Unit	Test Method
Cold Elongation (-25°C)	80	%	IEC 60811-1-4
Cold Impact (-25°C)	pass		IEC 60811-1-4
Hot Deformation (90°C)	1.5	%	BS 6469 99.1
Hot Pressure Test (90°C)	35	%	IEC 60811-3-1

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance			BS 6469 99.2
20°C	3.0E+14	ohms·cm
after 12 hours immersion in water : 20°C	2.0E+13	ohms·cm

Flammability	Nominal Value	Unit	Test Method
Acid Gas Emission Conductivity	18.0	µS/cm	IEC 60754-2
Acid Gas Emission pH	5.30		IEC 60754-2
Flammability Temperature Index	270	°C	ISO 4589-3
Smoke Density			ASTM E662
Flaming mode ³	< 91	Ds
Non-flaming mode ⁴	270	Ds
Toxicity	0.500		NES 713

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution	0.0	%	IEC 60754-1

Extrusion	Nominal Value	Unit
Draw Down	1.5:1.0
Extruder Screw Compression Ratio	1.0:1.0 to 2.0:1.0

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	6.50	kN/m	BS 6469 99.1

Aging	Nominal Value	Unit
Change in Tensile Strength in Air (110°C, 168 hr)	26	%
Change in Tensile Strain at Break in Air (110°C, 168 hr)	-6.0	%
Change in Tensile Stress
23°C, 168 hr, in IRM 902 Oil	-1.0	%
23°C, 168 hr, in IRM 903 Oil	-18	%
70°C, 4 hr, in IRM 902 Oil	-15	%
Change in Tensile Strain at Break
23°C, 168 hr, in IRM 902 Oil	-3.0	%
23°C, 168 hr, in IRM 903 Oil	-9.0	%
70°C, 4 hr, in IRM 902 Oil	-8.0	%
Change in Volume
23°C, 168 hr, in IRM 902 Oil	2.0	%
23°C, 168 hr, in IRM 903 Oil	6.0	%
70°C, 4 hr, in IRM 902 Oil	2.0	%

Electrical	Nominal Value	Unit	Test Method
Dielectric Constant (50 Hz)	3.80		ASTM D150
Dissipation Factor (50 Hz)	0.023		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	36	%	ISO 4589-2

Extrusion	Nominal Value	Unit
Drying Temperature	60.0 to 70.0	°C
Cylinder Zone 1 Temp.	135	°C
Cylinder Zone 2 Temp.	140	°C
Cylinder Zone 3 Temp.	145	°C
Cylinder Zone 4 Temp.	150	°C
Cylinder Zone 5 Temp.	160	°C
Melt Temperature	165 to 175	°C
Die Temperature	165	°C

Note Message
1 .	after 7 days at 110°C
2 .	after 7 days at 110°C
3 .	Time to maximum: 14 minutes
4 .	Time to maximum: 11 minutes

Resin Grade	Manufacturer	Category	Trademark
Polypropylene PP 10 CA	PETKIM Petrokimya Holding A.S.	PP, Unspecified	Polypropylene
Yanshan PE LD100	SINOPEC Beijing Yanshan Petrochemical	LDPE	Yanshan PE
BIOH™ Polyol X-0210	Cargill Industrial Bio-Products	Biodeg Polymers	BIOH™ Polyol
HIPOLEN P® EH 7	HIPOL A.D.	PP Homopolymer	HIPOLEN P®
Medalist® MD-53273 (PRELIMINARY DATA)	Teknor Apex Company	TPE	Medalist™