| PET+PC, non-reinforced, injection molding, improved impact strength |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 270°C, 2.00 mm 1 | 0.70 | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.30 | % | |
| Flow : 270°C, 2.00 mm 3 | 0.70 | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2200 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% Strain | 65.0 | MPa | ISO 178/A |
| 23°C | 75.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PET+PC, GHMPR, 09-020 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | < 10.0 | min | |
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Melting Temperature 8 | 250 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; WZ 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; WZ 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-132 | Matrix Polymers | LDPE | REVOLVE® |
| Trithene® TX 8024 | Petroquimica Triunfo | LDPE | Trithene® |
| BB-AMIDE 5011 | BB Resins S.r.l. | Nylon, Unspecified | BB-AMIDE |
| Flexalloy® 09-U0373R1-82NT1 | Teknor Apex Company | PVC, Flexible | Flexalloy® |
| Polyrocks 5003G15C | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |