ALCOM® PC + AWL 750/20.1 WT1407-04LB
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC + AWL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 599ydZ_ALCOM-PC-AWL-750-20-1-WT1407-04LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PC + AWL 750/20.1 WT1407-04LB is a Polycarbonate + ABS (PC+ABS) product filled with 20% filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PC + AWL 750/20.1 WT1407-04LB include automotive, electrical/electronic applications, lighting applications and reflectors. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 118 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 53.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 10 | % | |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 91 | % | DIN 5033 |
| Y10 of Transmittance : 500.0 µm | 0.10 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 100 to 110 | °C | |
| Desiccant Dryer | 100 to 110 | °C | |
| Drying Time | |||
| Circulation Dryer | 4.0 to 8.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2866T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| PRL PPX/NY-GP2 | Polymer Resources Ltd. | PPE+PS+Nylon | PRL |
| Hostacom TRC 364N C12752 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina WHITE COLOR CONCENTRATE MBU 10/1075-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Axiall PVC 3303 | Axiall Corporation | PVC, Rigid | Axiall PVC |