PENTAMID AHT MC30 H ungefärbt
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AHT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 58NwzU_PENTAMID-AHT-MC30-H-ungef-rbt.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 4.6, easy flow, 30% special mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.75 | % | ISO 294-4 |
| Flow direction | 0.75 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.4 | % | ISO 62 |
| Viscosity Number | 140 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 270 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Flexural Modulus | 9600 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 280 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 295 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | IEC 60250 | |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| ISO Description: PA4.6, MHR, 18-120 N, MD30The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 295 - 320 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Pressure | 70.0 | MPa | |
| Holding Pressure | 38.5 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUZEX® 7303 | SK Global Chemical | HDPE | YUZEX® |
| BJB Silicone TC-5040 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| LNP™ THERMOCOMP™ RF003XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 4260-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9785-79 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |