Plenco 03356 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 58NDcc_Plenco-03356-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.43 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ASTM D638 |
| Tensile Strength | 46.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 86.6 | MPa | ASTM D790 |
| Compressive Strength | 159 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21.2 | J/m | ASTM D256 |
| Notched Izod Impact | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 188 | °C | ASTM D648 |
| Continuous Use Temperature | 208 | °C | ASTM D794 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 12 | kV/mm | ASTM D149 |
| -- 2 | 7.8 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.064 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.15%Heat Resistance, ASTM D794: 208°CDrop Ball Impact, PLENCO Method: 88 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baytec® EDG-070D | Covestro - PUR | TSU | Baytec® |
| CEPLA CW-462E | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Hapflex™ 666 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| PCC HD 6070 UA | PCC Plastics & Consultations Center | HDPE | PCC |
| Durethan® B 30 S 000000 | LANXESS Corporation | Nylon 6 | Durethan® |