CERTENE™ LLBF-118A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 57tQxF_CERTENE-LLBF-118A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-118A is a certified prime resin with Butene-comonomer, designed for production of Blown films used in general purpose packaging. LLBF-118A features excellent combination of easy processability with good film strength as well as wide heat sealing temperature range. LLBF-118A applications include garment bags, produce bas and liners. LLBF-118A contains NO slip and NO antiblock. LLBF-118A complies with FDA regulation 21CFR 177.1520(c)3.2a, conditions of use A-H per 21CFR 176.170(c), Table 2. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 221 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 10.3 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 36.5 | MPa | ASTM D882 |
| TD : Break, 25 µm | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 550 | % | ASTM D882 |
| TD : Break, 25 µm | 700 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 150 | g | ASTM D1922 |
| TD : 25 µm | 300 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 35 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 18 | % | ASTM D1003 |
| Additional Information |
|---|
| 1.0 mil (25 µm) film; melt temperature 410-415°F; blow-up-ratio 2.5 :1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC FK 0635 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KOPLA PA66 KUG1330BK | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Hostaform® C 13031 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| IDI SMC S30 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Sumiliteresin® PR-55464 | SBHPP | Phenolic | Sumiliteresin® |