YUCLAIR® FU149M
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 57IC4O_YUCLAIR-FU149M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUCLAIR FU149M is butene-1 copolymer designed for use in general purpose film application. YUCLAIR FU149M provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FU149M shows superior tensile strength, tear strength, gel-free, antiblock and sealibility. Outstanding clarity and good processibility make this resin an ideal choice for film application when blended with conventional LDPE. YUCLAIR FU149M can be processed readily into blown film using standard extrusion techniques. YUCLAIR FU149M complies with FDA regulations in 21 CFR177.1520 for all food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | ASTM D746 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 11.8 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 50 µm | 42.2 | MPa | ASTM D882 |
| TD : Break, 50 µm | 35.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 750 | % | ASTM D882 |
| TD : Break, 50 µm | 850 | % | ASTM D882 |
| Spencer Impact (50.0 µm) | 0.981 | J | ASTM D3420 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1922 | ||
| MD : 50.0 µm | 49.0 | kN/m | ASTM D1922 |
| TD : 50.0 µm | 117.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 20 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Die Temperature | 190 - 195 | °C |
| Extrusion instructions |
|---|
| Film Extrusion Condition: Screw dia 50, Die dia 150, BUR 2.2Die gap 1.8, Screw RPM 45, L/S 7.2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STARLEX E/8025-86 naturale | Daloga srl | TPU-Polyether | STARLEX |
| Tenopom® POM B3 ST PRTA010 PR325 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Electrafil® J-80/CF/10/Natl | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |
| Karina CLEAR PVC COMPOUND -E 75/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID B S GV30 H natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |