Purac PLA Blend B

Category:	PLA , Polylactic Acid
Manufacturer:	Purac
Trademark:	Purac PLA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	56Q3Kp_Purac-PLA-Blend-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Homo PLA: improved modulus PLA blends based on monomers from Purac offer: Heat resistance up to 120°C (HDT B) Good processing economics Impact resistance comparable to ABS Biobased content Multiple end-of-life options Existing commercial availability Blend B: to achieve a higher modulus, and an even higher temperature resistance, talc was added to blend A (see blend B in the table below).

Message

Homo PLA: improved modulus

PLA blends based on monomers from Purac offer:

Blend B: to achieve a higher modulus, and an even higher temperature resistance, talc was added to blend A (see blend B in the table below).

General Information
Filler / Reinforcement	Talc
Additive	Nucleating Agent
Features	High Heat Resistance Homopolymer Nucleated Renewable Resource Content
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit
Density	1.27	g/cm³

Impact	Nominal Value	Unit
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²

Thermal	Nominal Value	Unit
Heat Deflection Temperature ¹(0.45 MPa, Unannealed)	120	°C

Injection	Nominal Value	Unit
Processing (Melt) Temp	190 to 220	°C
Mold Temperature	70.0 to 100	°C

Note Message
1 .	Flatwise

Resin Grade	Manufacturer	Category	Trademark
Sanren EVA 4.5/0.5	SINOPEC Shanghai Petrochemical Co. Ltd.	EVA	Sanren
Witcom PP 2007/117	Witcom Engineering Plastics B.V.	PP, Unspecified	Witcom PP
Xuchuan A-9003/B-6280	Xuchuan Chemical (Suzhou) Co., Ltd	TPU-Polyester	Xuchuan
Varcum 29317	Durez Corporation	Phenolic	Varcum
Arnite® TV4 441	DSM Engineering Plastics	PBT+PET	Arnite®