Durethan® BKV 230 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 55yYek_Durethan-BKV-230-DUS008-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.30 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.80 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.16 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.30 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.070 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.1 | 8.6 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7400 | 4200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 190 | 100 | MPa | |
| 23°C 6 | 205 | 125 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.8 | 6.6 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, MR, 14-080, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 13 | kJ/m² | |
| 23°C | 20 | 37 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 90 | kJ/m² | |
| 23°C | 85 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 15 | 15 | kJ/m² | |
| 23°C | 20 | 35 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 75 | 95 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 198 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V70SW | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| NEFTEKHIM PE 6148C (486H3) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Hifax TRC 341P | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 8600-85 Orange 584 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4215-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |