Silamid® SV15MF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 55GKor_Silamid-SV15MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, type reinforced with short glass fibres and filled with mineral filler, modificated, high rigidity, shape stability under heat, reduced flammability, natural, grey (RAL 7035), optimal flow properties. Suitable for injection mouldings in electrotechnics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.48 | 1.48 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 0.90 | 0.90 | % | |
| Flow | 0.40 | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.75 | 0.75 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7000 | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | 70.0 | MPa | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | 185 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | -- | 4.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | -- | 0.10 | IEC 60250 | |
| Arc Resistance | 120 | -- | sec | ASTM D495 |
| Comparative Tracking Index (Solution A) | -- | 400 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | V-2 | -- | UL 94 | |
| Glow Wire Ignition Temperature | 960 | 960 | °C | IEC 60695-2-13 |
| Needle Flame Test | 30.0 | 30.0 | sec | IEC 60695-2-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7990E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| K-Flex 3055 | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| Hostaform® S 9364 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Nylux 66-NAT | KMI Group, Inc. | Nylon 66 | Nylux |
| ALTECH® ABS A 1000/160 BK2448-12LS | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |