Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is a homopolymer and copolymer of Blenda heterophasic ethylene and propylene; specially designed for injection molding applications generally requiring excellent balance of properties between rigidity and impact resistance. This product has excellent processability and productivity.

Applications

Injection Molding, Automobile Applications, Battery case ; Toys; Household Appliances in general; Crates; Buckets; Base resin for compounding ; High impact resistance parts.

It exhibits a good fluidity combined with a good balance of impact and stiffness as well as a low warpage tendency. Even at sub-zero temperatures and also provides good surface properties and excellent processability.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Copolymer Good Flow Good Impact Resistance Good Processability Good Stiffness Good Surface Finish Low Temperature Resistant Low Warpage Nucleated
Uses	Appliances Automotive Applications Battery Cases Crates Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	13	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	70		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	20.0	MPa	ASTM D638
Tensile Elongation ²(Break)	4.0	%	ASTM D638
Flexural Modulus - 1% Secant	1000	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	30	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	90.0	°C	ASTM D648
Vicat Softening Temperature	148	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3975H	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Vipel® F764-PTH-20	AOC, L.L.C.	Polyester Alloy	Vipel®
Zhongfa PP FR-38	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
ARCEL® ULV (4.00 pcf)	NOVA Chemicals	PS+PE	ARCEL®
Huafon JF-S-DR9020	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon