TAROLOX 111 G3
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 537Tzw_TAROLOX-111-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOX 111 G3 is a Polyethylene Terephthalate (PET) product filled with 15% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 to 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.70 to 0.90 | % | |
| Flow | 0.30 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Granule Humidity 1 | < 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 9000 | MPa | ISO 178 |
| Flexural Stress 3 | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 218 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Ball Pressure Test (245°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 252 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 3.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (1.00 mm) | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 2752 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| TOTAL Polystyrene Crystal CX5243 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Mylar® J (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Hostaform® SXT90Z-02 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Plaslube® NY-1/MS/5 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |