Braskem PE SBC818R50
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 52YezO_Braskem-PE-SBC818R50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SBC818R50 is a low density polyethylene developed for coating process, it presents very good optical properties, low neck-in, good film stability, and good adhesion on porous substrate. Additives free. The minimum biobased content of this grade is 45%, determined according to ASTM D6866. Applications: Extrusion coating. Injection of general parts and carrier for masterbatches. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.1 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 70.0 | MPa | ASTM D882 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 380 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 870 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm, Blown Film) | 64 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (25 µm, Blown Film) | 56 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60 °, blown film) | 76 | ASTM D2457 | |
| Haze (Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 45 | % | ASTM D6866 |
| Blown Film Properties: 25 µm thick film, obtained from a 40 mm extruder, with blow up ratio of 2.2:1, die gap 1.8 mmRecommended process conditions:Extrusion coating Extruder type: Screw W/D ratio 20:1, Compression ratio 3 to 4:1 Temperature profile on horizontal extruder: Barrel: from 150 to 340°C, Die and melt mass: from 300 to 340°C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1704 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Ravaflex IIR | Ravago Group | IIR | Ravaflex |
| Deco-Coat™ 60-7185 | Epoxies, Etc. | Acrylic, Unspecified | Deco-Coat™ |
| Formolene® 6520N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| INNOPOL® PP CS 1-1240 | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |