Starex PT-0170 M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 523AGg_StarexPT0170M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex PT-0170 M is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 1.4 | g/10 min | ASTM D1238, ISO 1133 |
| 220°C/10.0 kg | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.60 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 111 | ASTM D785 | |
| R scale | 111 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 13.0 | MPa | ASTM D638 |
| Fracture | 15.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 14 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 60.0 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 88 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 460 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 280 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 94.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 103 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 80.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/B50 |
| -- | 101 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 T 40 FRO 3 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| WPP PP PPHFGC-3 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| ELASTOSIL® RT K | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Karina IVORY PVC COMPOUND -E 75900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® SSR1502-45 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |