Styrolux® T
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 51iWIs_Styrolux-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolux T is a new developmental, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux T has been developped for blending with a second SBC component, Styrolux S, which inceases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D | 60 | ASTM D2240 | |
| Shore D | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 910 | MPa | ASTM D638 |
| -- | 1200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 18.2 | MPa | ASTM D638 |
| Yield, 23°C | 25.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 260 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 250 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 862 | MPa | ASTM D790 |
| -- | 1000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 26.2 | MPa | ASTM D790 |
| -- | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 20 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 66.7 | °C | ASTM D1525 1 |
| -- | 62.0 | °C | ISO 306/A50 |
| -- | 46.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (550 nm) | 90.0 | % | ASTM D1003 |
| Haze | < 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Injection Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Quadrant EPP CESTICOLOR HD 500 | Quadrant Engineering Plastic Products | HMWPE | Quadrant EPP |
| Sinpolene MBW1781 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Fainplast PVC GK 91/2 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ESTOPLAST EP 4030BL09 | Ester Industries Ltd. | PBT | ESTOPLAST EP |