LNP™ COLORCOMP™ J1000AE compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 512DAh_LNP-COLORCOMP-J1000AE-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP J1000AE is an unfilled Polyethersulfone. Added feature of this grade is: Easy Molding. Also known as: LNP* COLORCOMP* Compound J-1000 EM Product reorder name: J1000AE |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2690 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 88.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 6.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2620 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 200 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.8E+15 | ohms·cm | ASTM D257 |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.7E-3 | ||
| 60 Hz | 1.7E-3 | ||
| 1 kHz | 2.2E-3 | ||
| 1 MHz | 5.6E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 A TFE 15 | RTP Company | Nylon 6 | RTP |
| SABIC® Polyester POY 221 | Saudi Basic Industries Corporation (SABIC) | PET | SABIC® HDPE |
| Surlyn® 1652SB | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| KRALASTIC® KU-670 R-2 | Nippon A&L Inc. | ABS | KRALASTIC® |
| Jam PE 10501 | Jam Petrochemical Company | VLDPE | Jam PE |