TES J-4/35
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 50wVqT_TES-J-4-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TES J-4/35 is a Polyamide 612 (Nylon 612) product filled with 35% glass fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TES J-4/35 include engineering/industrial parts, automotive, electrical/electronic applications, furniture and handles. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 40 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9650 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 9310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 248 | MPa | ASTM D790 |
| Compressive Strength | 159 | MPa | ASTM D695 |
| Shear Strength | 65.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 199 | °C | |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.70 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.024 | ||
| 1 MHz | 0.016 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 to 104 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 271 to 282 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Nozzle Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 54.4 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV-8251 | NuSil Technology | Silicone | NuSil |
| Celanex® 3216 | Celanese Corporation | PBT | Celanex® |
| Ceramer 20 | Ceramer GmbH | PPSU | Ceramer |
| HiFill® PA6 IM 811 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| HIPOLEN P® TM 21G | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |