Next Nylon 6 Industrial Series NG35-02BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 50nKh6_Next-Nylon-6-Industrial-Series-NG35-02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Nylon 6, Glass Fiber Reinforced Black compound Product Applications It is used in a wide variety of industries for applications, such as engine components in automotive. Benefits The product offers a good combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.40 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.25 | -- | % | ASTM D955 |
| Transverse flow | 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.4 | -- | % | ASTM D570 |
| Saturation 1 | 6.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 105 | -- | ASTM D785 | |
| Class r | 130 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 130 | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 8200 | 6100 | MPa | ASTM D790 |
| Flexural Strength | 190 | 150 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 98 | 130 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 210 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 170 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOMAMID® 66SN | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| FHR Polypropylene 13R9A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Hyundai EP PPF HT960 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Ingeo™ 3001D | NatureWorks® LLC | PLA | Ingeo™ |
| Sylvin 7833-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |