Ultramid® 8231G HS BK-106
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 50YU9V_Ultramid-8231G-HS-BK-106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons. Applications Ultramid 8231G HS BK-106 is ideally suited for more demanding performance applications such as washers, gears, engine and motor parts, chutes, and higher temperature environments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | |
| Water Absorption | |||
| 24 hr | 1.4 | % | ASTM D570 |
| 23°C, 24 hr | 1.4 | % | ISO 62 |
| Saturation | 8.1 | % | ASTM D570 |
| Saturation, 23°C | 8.1 | % | ISO 62 |
| Equilibrium, 50% RH | 2.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5800 | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 118 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4940 | MPa | ASTM D790 |
| 23°C | 5300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C | 3.8 | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 2.71 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 198 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Soarnol® E3808 | Soarus L.L.C. | EVOH | Soarnol® |
| Durethan® BKV 30 W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| INSTRUC PSUGF30HF | Infinity LTL Engineered Compounds | PSU | INSTRUC |
| LNP™ THERMOCOMP™ Lexan_JK500 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| LUVOCOM® 50-7856/FR/BK | Lehmann & Voss & Co. | PC | LUVOCOM® |