FINGERPRINT™ MDPE 7520 NT
| Category: | MDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | FINGERPRINT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4znBPO_FINGERPRINT-MDPE-7520-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FINGERPRINT™MDPE-7520 NT is a kind of Unipol™Bimodal polyethylene resin prepared by process II. This product is used for the processing of micro-irrigation tapes with thin-walled structures. Main features:
slip agent content: none opening agent content: none |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | > 0.15 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Film Puncture Energy 1(130 µm) | 6.10 | J | Internal method |
| Film Puncture Force 2(130 µm) | 146 | N | Internal method |
| secant modulus 3 | ASTM D882 | ||
| 1% secant, MD : 130 µm | 552 | MPa | ASTM D882 |
| 2% secant, MD : 130 µm | 448 | MPa | ASTM D882 |
| 1% secant, TD : 130 µm | 658 | MPa | ASTM D882 |
| 2% secant, TD : 130 µm | 527 | MPa | ASTM D882 |
| Tensile Strength 4 | ASTM D882 | ||
| MD : Yield, 130 µm | 18.8 | MPa | ASTM D882 |
| TD : Yield, 130 µm | 23.6 | MPa | ASTM D882 |
| MD : Fracture, 130 µm | 37.4 | MPa | ASTM D882 |
| TD : Fracture, 130 µm | 48.3 | MPa | ASTM D882 |
| Tensile Elongation 5 | ASTM D882 | ||
| MD : Fracture, 130 µm | 580 | % | ASTM D882 |
| TD : Fracture, 130 µm | 700 | % | ASTM D882 |
| Dart Drop Impact 6 | |||
| 130 µm | 510 | g | ASTM D1709A |
| 130 µm | 400 | g | ASTM D1709B |
| Elmendorf Tear Strength 7 | ASTM D1922 | ||
| MD : 130 µm | 640 | g | ASTM D1922 |
| TD : 130 µm | 1900 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 8(45°, 127 µm) | 7 | ASTM D2457 | |
| Haze 9(127 µm) | 76 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 243 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 挤塑机尺寸：2.5 英寸 (63.5mm)；30:1 L/D 比率 桶类型：平滑内膛 熔体温度：470°F (243°C) 模具直径：6 英寸 放大比：2.1 比 1 |
| Note Message | |
|---|---|
| 1 . | 2.1:1 BUR |
| 2 . | 2.1:1 BUR |
| 3 . | 2.1:1 BUR |
| 4 . | 2.1:1 BUR |
| 5 . | 2.1:1 BUR |
| 6 . | 2.1:1 BUR |
| 7 . | Method B;2.1:1 BUR |
| 8 . | 2.1:1 BUR |
| 9 . | 2.1:1 BUR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Boltaron 3042 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| Caltex PP MU42 | GS Caltex | PP, Unspecified | Caltex PP |
| Generic PEI - Glass Fiber | Generic | PEI | Generic |
| HiFill® PA6 GF14 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| ISOTHANE® 3065A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |