Bayblend® FR410 MT
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4zMaGE_Bayblend-FR410-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rubber modified PC blend; 10 % mineral filled; flame-retardant; Vicat/B 120 = 108 °C; very good UL recognition in small wallthickness (V-0 at 0.75 mm); for railway interiors. Due to the special formulation of this grade, the final parts may require coating. Please contact us directly regarding classifications according to the respective rail standards. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm | 0.40 to 0.50 | % | |
| Flow : 260°C, 3.00 mm | 0.40 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3950 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 63.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 19 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/B50 |
| -- | 108 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.8E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 5.9E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 360 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® 500750M | ELASTO | SEBS | Mediprene® |
| RheTech Thermoplastic Polyolefin FT6140-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Versaflex™ 9545-1 | PolyOne Corporation | TPE | Versaflex™ |
| Generic PP Homopolymer - Glass\Mica | Generic | PP Homopolymer | Generic |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7104BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |