High molecular weight general purpose polystyrene combining high heat resistance and good mechanical strength.

Suitable for direct gassing extrusion, for biaxially oriented films and sheets, for glass clear sheets and panels.
Also used in injection moulding of medium—thickness wall transparent parts.

Designation: Thermoplastics ISO 1622-PS,G,105-03

Applications
Uses range from foamed packaging trays, clear panels for shower cabins, insulation boards (XPS), OPS for labels and packaging to moulded fridge clear components, Petri dishes, technical parts.

General Information
Features	High molecular weight Good strength Heat resistance, high Compliance of Food Exposure General
Uses	Bi-axially Oriented Film Clear Sheet Engineering accessories Sheet Transparent or Translucent Accessories Medical/nursing supplies Reinforced panel Bracket tray
Agency Ratings	Europe No 10/2011
UL File Number	E83071
Appearance	Clear/transparent
Forms	Particle
Processing Method	Film extrusion Extrusion Sheet extrusion molding Thermoforming Profile extrusion molding Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Heat vs. Temperature (ISO 11403-2) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Apparent Density	0.65	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	2.0	g/10 min	ISO 1133
Molding Shrinkage	0.30 - 0.60	%	Internal method
Water Absorption (23°C, 24 hr)	< 0.10	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	80		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3350	MPa	ISO 527-2/1
Tensile Stress (Break)	49.0	MPa	ISO 527-2/5
Tensile Strain (Break)	2.5	%	ISO 527-2/5
Flexural Stress ¹	91.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ISO 180/1A
-30°C	1.7	kJ/m²	ISO 180/1A
23°C	1.9	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed)	95.0	°C	ASTM D648
Vicat Softening Temperature
--	106	°C	ISO 306/A50
--	101	°C	ISO 306/B50
CLTE - Flow	7.0E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.17	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.5E+15	ohms	IEC 60093
Volume Resistivity	> 7.0E+15	ohms·cm	IEC 60093
Dielectric Strength	70	kV/mm	IEC 60243-1
Dielectric Constant (50 Hz)	2.50		IEC 60250
Dissipation Factor (50 Hz)	2.0E-4		IEC 60250
Comparative Tracking Index (Solution A)	425	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, All Colors)	HB		UL 94
Glow Wire Ignition Temperature (1.60 mm)	650	°C	IEC 60695-2-13

Additional Information	Nominal Value
Designation	Thermoplastics ISO 1622-PS,G,105-03

Injection	Nominal Value	Unit
Processing (Melt) Temp	220 - 270	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Predrying normally not required

Extrusion	Nominal Value	Unit
Melt Temperature	210 - 240	°C

Note Message
1 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
Malen E FGNX 23-D006	LyondellBasell Industries	LDPE	Malen
TPC PVC SP66J	Thai Plastics and Chemicals Public Company Limited	PVC Homopolymer	TPC PVC
Elastollan® S98AN	BASF Corp. Thermoplastic Polyurethanes	TPU-Polyester	Elastollan®
Enable™ 20-05HH	ExxonMobil Chemical	mPE	Enable™
Plaslube® POM CO GF20 TL20	Techmer Engineered Solutions	Acetal (POM) Copolymer	Plaslube®