Cellidor B 531-07
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | Cellidor |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4yXxRf_Cellidor-B-531-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cellidor B 531-07 is a Cellulose Acetate Butyrate (CAB) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (210°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 42.0 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Stress (3.5% Strain) | 52.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C | |
| Die Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 R3 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| TRANSMARE® 19HT40-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| ULTEM™ 1010F resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| DOMAMID® 6STZX | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| InnoFR™ FX-8071 | Innovative Polymers, Inc. | TSU | InnoFR™ |