Akulon® Ultraflow K-FKGV4 /A
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® Ultraflow |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4yXK9v_Akulon-Ultraflow-K-FKGV4-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® Ultraflow K-FKGV4 /A is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber. It is available in Asia Pacific or Europe. Important attributes of Akulon® Ultraflow K-FKGV4 /A are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.60 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 2.0 | -- | kJ/m² | |
| 23°C | 2.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 30 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 185 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | 10.0 | ||
| 1 MHz | 3.80 | 3.90 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | 0.30 | ||
| 1 MHz | 0.021 | 0.10 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.800 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 235 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 250 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 235 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTORAN® 1900 | Evonik Industries AG | PPE | VESTORAN® |
| ARK 2150-40A | Arkadia Plastics, Inc. | TPU, Unspecified | ARK |
| Diakon® CLG356L | Lucite International Inc. | Acrylic (PMMA) | Diakon® |