LNP™ STAT-LOY™ AX11421 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4yLLz9_LNP-STAT-LOY-AX11421-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic. Also known as: LNP* STAT-LOY* Compound AX11421 Product reorder name: AX11421 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 2.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 3.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1410 | MPa | ASTM D638 |
| -- | 1320 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 30.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/5 |
| Break 3 | 21.0 | MPa | ASTM D638 |
| Break | 21.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2/5 |
| Break 5 | 48 | % | ASTM D638 |
| Break | 81 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1350 | MPa | ASTM D790 |
| -- 7 | 1330 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 44.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D256 |
| 23°C 9 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 29.0 | J | ASTM D3763 |
| -- | 20.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 86.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 69.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 67.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 to 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 24809 | Teknor Apex Company | TPV | Sarlink® TPV |
| Unichem 7884H | Colorite Polymers | PVC, Unspecified | Unichem |
| Sylvin 6177-80 Blue 8368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4200-70 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8773-60D Grey 9509 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |