Comco PA 6 G heat stabilized
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Comco-Plastic GmbH |
| Trademark: | Comco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4yDYg3_Comco-PA-6-G-heat-stabilized.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Comco PA 6 G heat stabilized is a Polyamide 6 (Nylon 6) material. It is available in Europe. Important attributes of Comco PA 6 G heat stabilized are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ||||
| Saturation, 23°C | 6.6 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| after 24 h immersion in water : 23°C | 50.0 | -- | mg | |
| after 96 h immersion in water : 23°C | 94.0 | -- | mg |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum Service Temperature | ||||
| in air continuosly | 120 | -- | °C | |
| in air for short periods | 170 | -- | °C | |
| Service Temperature - Minimum | -40 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | -- | ISO 2039-2 | |
| Shore Hardness (Shore D) | 80 | -- | ISO 868 | |
| Ball Indentation Hardness | 160 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 80.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 15 | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 21.0 | 10.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604 | |||
| 5% Strain | 85.0 | -- | MPa | |
| 2% Strain | 48.0 | -- | MPa | |
| 1% Strain | 25.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength | 3.5 | 6.0 | kJ/m² | ISO 180/2A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | |
| CLTE - Flow | ||||
| 23 to 60°C | 8.0E-5 | -- | cm/cm/°C | |
| 23 to 100°C | 9.0E-5 | -- | cm/cm/°C | |
| Thermal Conductivity | 0.29 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | > 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.60 | 6.60 | ||
| 1 MHz | 3.20 | 3.70 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.012 | 0.14 | ||
| 1 MHz | 0.016 | 0.050 | ||
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- | ||
| Oxygen Index | 25 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 1% Strain |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex WR-9100 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| 4MID® 9A32335 I | 4Plas | Nylon 66 | 4MID® |
| Fusabond® C250 | DuPont Packaging & Industrial Polymers | EVA | Fusabond® |
| LOFEX® A3111 | Lotte Chemical Corporation | PET | LOFEX® |
| Petrothene® XL07505 | LyondellBasell Industries | EVA | Petrothene® |