Braskem PE IF 33
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4wiBeO_Braskem-PE-IF-33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IF33 is a Linear Low Density Polyethylene, narrow molecular weight butene-1 copolymer, produced by solution process, for injection molding applications. It offers high fluidity, good flexibility and low warpage. It contains antioxidant additive. Application: Resin has been specifically developed for injection molding lids seal and lids for food containers, housewares, containers and general purpose. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.931 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 48 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 10% Igepal, Compression Molded, F50) | < 1.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 15.0 | MPa | |
| Break, Compression Molded | 9.00 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 14 | % | |
| Break, Compression Molded | 100 | % | |
| Apparent Bending Modulus | 490 | MPa | ASTM D747 |
| Flexural Modulus - 1% Secant (Compression Molded) | 540 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 46.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 A-200 Z | RTP Company | PESU | RTP |
| RTP EMI 331 C FR | RTP Company | PC | RTP |
| Sizzle™ HF | Plastic Selection Group, Inc. | PS (GPPS) | Sizzle™ |
| COSMOPLENE® FS6612L | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP, Unspecified | COSMOPLENE® |
| LNP™ THERMOCOMP™ DX11355 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |