Plaslube® PEEK TL20 A
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4wQIdX_Plaslube-PEEK-TL20-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PEEK TL20 A is a Polyetheretherketone (PEEK) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.16 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.9 | % | ASTM D638 |
| Flexural Modulus | 3030 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 157 | °C | ASTM D648 |
| CLTE - Flow | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 249 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 360 to 388 | °C | |
| Middle Temperature | 360 to 388 | °C | |
| Front Temperature | 360 to 388 | °C | |
| Processing (Melt) Temp | 360 to 382 | °C | |
| Mold Temperature | 177 to 218 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE H645 | Dongbu Hannong Chemical | PS (HIPS) | SOLARENE |
| Moplen HP325M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Tarnamid® T- 30 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| THERMOLAST® K TF9CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Paracril® P7072P | INSA | NBR | Paracril® |