Order Products : sales@su-jiao.com
KumhoSunny ABS HFA700HT
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4wQ6gg_KumhoSunny-ABS-HFA700HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HFA700HTis high heat resistance enviromental flame retardant ABS resin. It has balance mechanical properties and a wide processing window. HFA700HT is mainly used in temperature controller, electron parts,etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 2.10 mm | V-0 | ||
| 3.20 mm | V-0 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 to 210 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 210 to 225 | °C | |
| Nozzle Temperature | 210 to 225 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2500.5 | RTP Company | PC+ABS | RTP |
| Radilon® A USX016W 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| Hiprolon® 70 VN | Arkema | Nylon 610 | Hiprolon® |
| Idemitsu PS SEHI-105 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| INLUBE PPSTF20 | Infinity LTL Engineered Compounds | PPS | INLUBE |