Fortron® 1342L4
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4wFu6V_Fortron-1342L4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 1342L4 is a low wear grade, ideally suited for bearings, gears and other sliding friction/wear applications. This product is glass fiber reinforced and contains PTFE. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.70 | g/cm³ | ASTM D792 |
| -- | 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14400 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 152 | MPa | ASTM D638 |
| Fracture | 165 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture | 1.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13700 | MPa | ISO 178 |
| Flexural Stress 1 | 245 | MPa | ISO 178 |
| Coefficient of Friction | |||
| Dynamic 2 | 0.21 | ASTM D1894 | |
| Dynamic 3 | 0.28 | ASTM D1894 | |
| Static 4 | 0.31 | ASTM D1894 | |
| Static 5 | 0.27 | ASTM D1894 | |
| With steel-dynamic 6 | 0.16 | ASTM D1894 | |
| With steel-static 7 | 0.20 | ASTM D1894 | |
| With steel-static | 0.20 | ISO 8295 | |
| Wear Factor 8 | ASTM D3702 | ||
| 416 Stainless : 32°C | 166 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 49°C | 323 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 93°C | 825 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specimen Thickness - Shrinkage | 3.18 | mm | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.5 | kJ/m² | ISO 180/1A |
| 23°C | 8.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 268 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 9 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 10 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 3 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 4 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 5 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 6 . | 73°F, 5 lbf, 5 in |
| 7 . | 73°F, 5 lbf, 5 in |
| 8 . | 16 µ-in, PV2000, 40 psi, 50ft/min |
| 9 . | 10°C/min |
| 10 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3024 GU6L1 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Alcryn® 3055 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| Braskem PP C719-35RNHP | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Elastollan® A C 85 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Monprene® CP-30120 XRD (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |