LNP™ KONDUIT™ PX10323 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4w3B3X_LNP-KONDUIT-PX10323-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive, electrically conductive mineral filled PA6 compound Also known as: LNP* KONDUIT* Compound PX10323 Product reorder name: PX10323 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.15 | % | |
| Across Flow : 24 hr | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10800 | MPa | ASTM D638 |
| -- | 16000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 54.0 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.0 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 12400 | MPa | ASTM D790 |
| -- 5 | 14000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 26 | J/m | ASTM D256 |
| 23°C 7 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D4812 |
| 23°C 8 | 8.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 186 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 200 | °C | ISO 75-2/Af |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 1.4E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 80°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| -- 10 | 3.5 | W/m/K | ASTM E1461 |
| -- 11 | 15 | W/m/K | ASTM E1461 |
| -- 12 | 1.5 | W/m/K | ISO 22007-2 |
| -- 13 | 18 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 650 | °C | |
| 1.60 mm | 960 | °C | |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 3.00 to 9.00 | MPa | |
| Screw Speed | 30 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | through-plane, 10*10*3mm sample |
| 11 . | in-plane, ø25*0.4mm disc |
| 12 . | through-plane, 60*60*3mm plaque |
| 13 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SI-LINK™ AC DFDB-5451 NT | The Dow Chemical Company | PE, Unspecified | SI-LINK™ |
| Moplen HP648S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Wellamid® MR409 22H-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| PLEXIGLAS® Sheet Optical RP Control 7D009 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |
| LEXAN™ 500R resin | SABIC Innovative Plastics | PC | LEXAN™ |