Clariant Nylon 6/12 612G43-L
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/12 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4vE3Zd_Clariant-Nylon-6-12-612G43-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Nylon 6/12 612G43-L is a Polyamide 612 (Nylon 612) material filled with 43% glass fiber. It is available in North America for injection molding. Primary attribute of Clariant Nylon 6/12 612G43-L: Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| Melting Temperature | 212 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150RMC65 | Technical Polymers, LLC | PPS | Thermec™ |
| XANTAR® G4F 25 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Altuglas® BS 645 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| E-Pos 101X75 | Epocat Nederland BV | Epoxy | E-Pos |
| Hanwha Total PE P200CB | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |