Skyrol® SM40
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4vC75B_Skyrol-SM40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SM40 is a transparent film with excellent handling characteristics and widely used in stamping foil, metallizing, and metallic yarn applications. SM40 has high resistance to the neckdown or creasing caused by high temperature and high tension coating operation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | |||
| Flow : 190°C, 20 min, 0.0120 mm | 2.8 | % | Internal Method |
| Flow : 190°C, 20 min, 0.0150 mm | 2.6 | % | Internal Method |
| Flow : 190°C, 20 min, 0.0190 mm | 2.6 | % | ASTM D955 |
| Flow : 190°C, 20 min, 0.0230 mm | 2.6 | % | ASTM D955 |
| Across Flow : 190°C, 20 min, 0.0120 mm | -0.40 | % | Internal Method |
| Across Flow : 190°C, 20 min, 0.0150 mm | -0.30 | % | Internal Method |
| Across Flow : 190°C, 20 min, 0.0190 mm | -0.30 | % | ASTM D955 |
| Across Flow : 190°C, 20 min, 0.0230 mm | -0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.40 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Dynamic 4 | 0.40 | ||
| vs. Itself - Dynamic 5 | 0.40 | ||
| vs. Itself - Static 6 | 0.40 | ||
| vs. Itself - Static 7 | 0.40 | ||
| vs. Itself - Static 8 | 0.50 | ||
| vs. Itself - Static 9 | 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 12 µm | 269 | MPa | |
| MD : Yield, 15 µm | 269 | MPa | |
| MD : Yield, 19 µm | 255 | MPa | |
| MD : Yield, 23 µm | 234 | MPa | |
| TD : Yield, 12 µm | 228 | MPa | |
| TD : Yield, 15 µm | 234 | MPa | |
| TD : Yield, 19 µm | 241 | MPa | |
| TD : Yield, 23 µm | 234 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 120 | % | |
| MD : Break, 15 µm | 130 | % | |
| MD : Break, 19 µm | 130 | % | |
| MD : Break, 23 µm | 150 | % | |
| TD : Break, 12 µm | 130 | % | |
| TD : Break, 15 µm | 140 | % | |
| TD : Break, 19 µm | 130 | % | |
| TD : Break, 23 µm | 130 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 12.0 µm | 164 | ||
| 15.0 µm | 162 | ||
| 19.0 µm | 164 | ||
| 23.0 µm | 164 | ||
| Transmittance | ASTM D1003 | ||
| 12.0 µm | 90.0 | % | |
| 15.0 µm | 90.0 | % | |
| 19.0 µm | 90.0 | % | |
| 23.0 µm | 90.0 | % | |
| Haze | ASTM D1003 | ||
| 12.0 µm | 2.9 | % | |
| 15.0 µm | 3.4 | % | |
| 19.0 µm | 3.4 | % | |
| 23.0 µm | 3.5 | % |
| Note Message | |
|---|---|
| 1 . | 19 µm |
| 2 . | 23 µm |
| 3 . | 19 µm |
| 4 . | 15 µm |
| 5 . | 12 µm |
| 6 . | 12 µm |
| 7 . | 23 µm |
| 8 . | 15 µm |
| 9 . | 19 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9058-90UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wellamid® GF33A099-HRN | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| APEX® 6500-105 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina IVORY PVC COMPOUND 551D35/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Escorene™ Ultra UL 00114 | ExxonMobil Chemical | EVA | Escorene™ Ultra |