AKROMID® A3 GK 40 1 natural (1803)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4upyAX_AKROMID-A3-GK-40-1-natural-1803-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GK 40 1 natural (1803) is a 40% glass bead reinforced, heat stabilised polyamide 6.6 with low warpage, high surface appearance and light inherent color Applications areas are highly integrated housings in the appliance industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 | % | |
| Flow | 1.3 | % | |
| Water Absorption (Saturation, 23°C) | 5.1 | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.8 | % | ISO 1110 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 40 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5800 | MPa | ISO 178 |
| Flexural Stress 2 | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | °C | DIN EN 11357-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aplax P0060CN | Ginar Technology Co., LTD. | PP, High Crystal | Aplax |
| Exelene® LDPE 6001 | Montachem International, Inc. | LDPE | Exelene® LDPE |
| Hifax TYC 1168X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| POLLITE 1002G30 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| ISOPAK® 525 Black | Great Eastern Resins Industrial Co., Ltd. (GRECO) | ABS | ISOPAK® |