Safrene® F 7650
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4u5qV4_Safrene-F-7650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene® F 7650 High Density Polyethylene Resin is a medium molecular mass grade with good processing properties. It exhibits good impact strength and environmental stress-crack resistance. Safrene® F 7650 High Density Polyethylene Resin is recommended for all general purpose applications up to 20 liter in volume. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.33 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 1.6 | g/10 min | ISO 1133 |
| Spiral Flow | 32.0 | cm | Internal method |
| Viscosity Number (Reduced Viscosity) | 280.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 23.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 19.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, molded | 8.0 | kJ/m² | ISO 179 |
| 23°C, molded | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Additional Information |
|---|
| Blow Molding conditions: Feed Zone: 160 to 180°C Zone 1: 170 to 190°C Zone 2: 180 to 200°C Zone 3: 180 to 190°C Die: 180 to 190°C Melt Temperature: 180 to 190°C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AESNO P20 TL | Arkema | Nylon 12 | Rilsan® |
| RTP PA66 50 GF BLK | RTP Company | Nylon 66 | RTP |
| Xuchuan XCS-2009S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Kepital® LX-30 BK | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| OmniCarb™ PC/PBT 1214 IM | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |