Moplen EP647N
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4rK94Q_Moplen-EP647N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen EP647N is a polypropylene impact copolymer manufactured using the Spheripol process. This grade has high gloss and contains antistatic agent Typical applications include injection molding of electrical appliance parts, toys and containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 1570 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 49 | J/m | |
| 23°C | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® T331C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| TEREZ PC 9005 SZ | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| TRIMID® N6-200L | Polymer Technology and Services, LLC | Nylon 6 | TRIMID® |
| Utomer UT81P80A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| MAJORIS FFR057 - 3717 | AD majoris | PP, Unspecified | MAJORIS |