LNP™ LUBRICOMP™ DBL349E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4pz5Ss_LNPLUBRICOMPDBL349Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DBL-4034 EM FR Product reorder name: DBL349E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.69 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.54 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 2970 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 41.4 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2 |
| Fracture | 37.9 | MPa | ASTM D638 |
| Fracture | 38.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638, ISO 527-2 |
| Fracture | 9.0 | % | ASTM D638 |
| Fracture | 7.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Stress | 78.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.52 | ASTM D3702 Modified | |
| With Self-Static | 0.70 | ASTM D3702 Modified | |
| Wear Factor - Washer | 90.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.7 | J | ASTM D3763 |
| -- | 4.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 129 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 129 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Quadrant EPP ERTALON® 66 SA | Quadrant Engineering Plastic Products | Nylon 66 | Quadrant EPP |
| SINOF P265U | SINOF HI-TECH MATERIAL CO. LTD | PPS | SINOF |
| ADDILENE J 380 | ADDIPLAST | PP Copolymer | ADDILENE |
| Bayblend® FR3009 | Covestro - Polycarbonates | PC+ABS | Bayblend® |