LNP™ THERMOCOMP™ DX13006 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4p8DeI_LNP-THERMOCOMP-DX13006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DX13006 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound DX13006 Product reorder name: DX13006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 90.0 | MPa | |
| Break | 85.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.7 | % | |
| Break | 3.4 | % | |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress | 144 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 4.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 137 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC501 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| SCLAIR® 2710 | NOVA Chemicals | HDPE | SCLAIR® |
| Thermoset Plastics EP-356 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Generic Acrylic (PMMA) | Generic | Acrylic (PMMA) | Generic |
| POLYCOMPO PP J136 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |