LG ASA LI951
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4mFnhg_LG-ASA-LI951.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ASA LI951 is an acrylonitrile-styrene-acrylate (ASA) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG ASA LI951 are:
The typical application areas of LG ASA LI951 are: automotive industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 25 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 77.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 120 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 104 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 68.6 - 88.3 | MPa | |
| Screw Speed | < 80 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205A HS | RTP Company | Nylon 6 | RTP |
| Synprene™ RT-5190 RoHS Black | PolyOne Corporation | SBC | Synprene™ |
| Xuchuan XCW-90HN | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ACCUGUARD™ HP0369V2CSL | ACLO Compounders Inc. | PP Homopolymer | ACCUGUARD™ |
| Sylvin 8280-90 Grey 9583 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |